Déanta ábhar aispeiste Fiber, rubair agus teas-resisting ábhar, comhbhrúite le páipéar tiubh.
|
:
4600 x 1500 x (0.3 - 6.0) mm, 4100 x 1500 x (0.3 - 6.0) mm
3800 x 2700 x (0.3 - 6.0) mm, 2000 x 1500 x (0.5 - 6.0) mm
1500 x 1360 x (0.5 - 6.0) mm, 3810 x 1270 x (0.5 - 6.0) mm
1270 x 1270 x (0.5 - 6.0) mm, 1500 x 1500 x (0.5 - 6.0) mm
Tá an méid eile roghnach nó de réir riachtanais na gcustaiméirí.
Pacáil:i pailléid adhmaid de thart ar 1000 kg, 2000kgs glan gach.
|
Bileoga rubair aispeiste Maoin Fhisiciúil
GB / T 3985-2008 |
||||||||
|
Mír
|
KXB510
|
KXB450
|
KXB400
|
KXB350
|
KXB300
|
KXB250
|
KXB200
|
KXB150
|
|
Neart teanntachta MPa
|
21.0
|
18.0
|
15.0
|
12.0
|
9.0
|
8.0
|
6.0
|
5.0
|
|
Comhéifeacht Aging
|
0.9
|
|||||||
|
Caillteanas Dó%
|
28.0
|
30.0
|
||||||
|
Ráta comhbhrúiteachta%
|
7-17
|
|||||||
|
Ráta Aisghabhála%
|
45
|
40
|
35
|
|||||
|
Ráta scíthe creep%
|
50
|
|||||||
|
Dlús g / cm3
|
1.6 - 2.0
|
|||||||
|
Ráta sceitheadh nítrigine
[ml / (h.mm)]
|
500
|
|||||||
|
Friotaíocht teasa agus brú
|
le teocht 500-510
agus an brú de 13-14MPa, Coinnigh ar feadh 30 nóiméad gan puncture
|
le teocht 440-450
agus an brú 11-12MPa, Coinnigh ar feadh 30 nóiméad gan puncture
|
leis an teocht 390-400
agus brú na8-9 MPa, Coinnigh ar feadh 30 nóiméad gan puncture |
le teocht 340-350
agus brú na7-8 Mpa, Coinnigh ar feadh 30 nóiméad gan puncture |
le teocht 290-300
agus brú na4-5 MPa, Coinnigh ar feadh 30 nóiméad gan puncture |
le teocht 240-250
agus brú na3-4Mpa, Coinnigh ar feadh 30 nóiméad gan puncture |
le teocht 190-200
agus brú na2-3MPa, Coinnigh ar feadh 30 nóiméad gan |
le teocht 140-150
agus brú na 1.5-2MPa,Keep for 30 min without puncture
|